Macroporous plaster, for ecological building, fibre-reinforced, based on hydraulic lime, for dehumidification and hygrometric rehabilitation of buildings and walls, in ecological building interventions, new buildings and in the restoration of vintage buildings and monuments.
Specification for Mortar for Masonry - Mortars for renovations (R)
Sanageb - Prodotti naturali per la Bioedilizia
Product of the Sanageb line, the line of products from Azichem Srl dedicated to green-building, ecological sanitation, thermal insulation and energy saving products since 1994.
Shelf-life: 12 months
Maximum diameter of aggregate: 1.5 mm
Mix with water: 16-18 %
Min. recommended thickness: 2 cm
Temperature of use: +6 / +30 °C
Static elastic modulus
Reaction to fire
> 4.5 N/mm²
- Light rosé (7,5 YR 8/2 Munsell® Soil Color Chart)
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
SANATIGH is a product consisting of hydraulic lime, botticino, kaolin, very fine calcium, expanded lightweight aggregates of volcanic origin, fiber-reinforced with special glass microfibres and fibers READYMESH PM 060. It has high hygroscopicity and breathability, contains no cements, resins, solvents and radioemissive substances. It has strong dehumidifying capacities and, thanks to the total absence of cement, is perfectly compatible with all types of masonry and especially with the historical walls and in all the interventions designed according to the canons of green building.
Approximately 12 kg/m² of SANATIGH for every centimetre of thickness to be implemented (minimum thickness 2 cm = 24 kg/m²).
Breathable dehumidifying plastering for wall bodies.
Removal of crumbling plaster, if present, up to a maximum height of about 1 metre, with respect to the line of persistent humidity; wall bodies of application must in any case be clean, intact, dust-free, fouling, crumbling and non-adhering parts, conveniently saturated with water until they reach the condition of "saturated with dry surface".
In the presence of salt efflorescence it will be necessary to ensure it is carefully removed by applying packs of the specific detergent and saline converter DETERG-A, in solution with water of 1:4. To prevent any new spills of salts, use specific universal anti-saline treatments in aqueous solution, SANAREG, for humid surfaces, or solvent-based, FEST SALZ, for cohesive saline concretions but with perfectly dry surfaces.
PREPARATION OF THE WALL SURFACE
• Remove all inconsistent, friable and rotten material, and grouting from joints, paying utmost attention where they are particularly friable or inconsistent (see also the paragraph on PREPARING SUPPORTS).
• In case of strong salt concentrations, read the paragraph on PREPARING SUPPORTS.
The sprayed rough coat must create a rough, corrugated surface to facilitate the adhesion of the following plaster, which must be applied promptly; within 1 - 2 days from the application of the rough coat. This adhesion spray must be applied with a low thickness (of a few millimetres) using a plastic-fluid consistency, and can be applied with the same SANATIGH product mixed with about 20% water. In case of particularly deteriorated masonry, it is recommended to use a specific UNTERSANA product to make the rough coat.
The following application of SANATIGH must be made before the complete hardening of the rough coat (within 24-48 hours if the rough coat is made with SANATIGH, and 12-24 hours if made with UNTERSANA).
Put about 2/3 of the mixing water into the mixer, and then gradually add SANATIGH and the remaining water, continuing to mix into a homogeneous, lump-free mixture of the desired consistency for trowel or plastering machine application. Indicatively, the necessary mixing water is 16-18% by weight (i.e. 4 - 4.5 litres per 25 kg bag).
Application can be performed by manual (trowel, plastering trowel) or mechanical spray methods. In case of application with a plastering machine, in order to allow adequate and homogeneous product mixing, it is recommended to not use machines with a continuous cycle, and to adjust nozzle, air and spray power in order to softly and lightly apply the product without excessive compaction.
Levelling of plastered surfaces with SANASTOF: green-construction fine, highly breathable mortar, natural hydraulic lime based with special, light, spherical micro-aggregates and high strength microfiber READYMESH PM 060.
Protect surfaces from fresh direct exposure to sunlight, from the rain and wind. Cure the prolonged moist hardening.
For thicknesses in excess of the 2 cm, and to improve the anti-cracking potential, provide for inserting a suitable reinforcement plaster-holding mesh: ARMAGLASS 140 o, recommended, a galvanized steel wire mesh with 2mm diameter, mesh 5x5 cm.
- Brick trowel
- Finishing trowel
- Plastering machine
- Mixed walls (bricks and stones)
- Stone walls
Dehumidifying, thermo-insulating plaster (800 kg/m³), with a natural hydraulic lime base. Ideal for hygrometric, anti-condensate renovation of internal walls (overground and underground).
Breathable plaster (1500 kg/m³), with a natural hydraulic lime base. Ideal for plastering overground or underground walls, both indoors and outdoors.
Thermo-insulating, dehumidifying plaster (600 kg/m³) with a natural hydraulic lime base, expanded perlite and cork flour. Ideal for thermo-insulating, anti-condensate renovation of external walls overground. Absolutely recommended!
Structural plaster (1700 kg/m³), dehumidifying, with a grey cement base. Ideal for reinforced grout on old walls.
Structural plaster (1700 kg/m³), dehumidifying, with a pure white cement base. Ideal for reinforced grout on old walls and the re-construction of overhanging roofs, belt courses, cornices, etc.