Code: REP.0133
Components: 1
Appearance: Powder
Structural, thixotropic, rheoplastic, composite cement mortar, based on high-resistance cements, superpozzolanic fillers, polymeric modifiers, anti-shrink agents, plasticisers, stabilisers, anti-corrosive, anti-allergic additives, selected aggregates, polypropylene fibres.
EN 998-1
Specification for Mortar for Masonry - General purpose rendering/plastering mortar (GP)
EN 1504-3
Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)
Maximum diameter of aggregate: 1.5 mm
Min. recommended thickness: 5 mm
Shelf-life: 12 months
Pot-life: 60 min
Max. recommended thickness: 3-4 cm
Nonflammable
Use wearing protective gloves
Temperature of use: +5 / +35 °C
Mix with water: 15 %
UV-resistant
Reaction to fire
A1 _
Bonding force
> 2 N/mm²
Capillary absorption
0.50 kg•h^0.5/m²
Darcy impermeability
1 x 10 E-10 cm/s
pH
> 12.5 _
Density
2170 kg/m³
Skid resistance
51 mm
Chloride content
<0.01 %
Static elastic modulus
> 21000 N/mm²
Compressive strength
> 60 N/mm²
Determination of thermal compatibility
1.6 mPa
Resistance to carbonatation
1.5 mm
Water/binder ratio
0.38 _
Flexural strength
> 6.5 N/mm²
- Gray
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
Restorations and repairs, structural recovery, reinforcement reconstruction, construction of reliable and durable coatings for building, civil, hydraulic, industrial, concrete and masonry works.
Application surfaces should be clean, free of dirt, crumbling and non-adhering parts, dust etc., and saturated with water "saturated with dry surface".. It is advisable to previously to apply the realkalising reinforcement CONSILEX SAN on the exposed surfaces, before they are restored.
Pour 2/3 of the total mixing water(about 3 litres per bag) in the concrete mixer, gradually add the product and the remaining water, until a homogeneous lump-free mixture of the desired consistency is obtained. Cure the protection and the prolonged moist hardening of exposed surfaces.
The addition of BOND HG to the mixing water (at a rate of approximately 0.5-0.7 kg for each lot of product) allows substantial improvements in terms of adherence, adhesion, watertightness, workability, moldability and capacity of deformation.
- Brick trowel
- Finishing trowel
- Shotcrete machine
- Plastering machine
- Spatula
High coating thicknesses, static, monolithic requirements, etc., it may be necessary to resort to appropriate reinforcements (electrowelded mesh etc.) anchored to the support with SYNTECH PROFIX or GROUT MICROJ or REPAR TIX G2.
REPAR TIX G2
Thixotropic cement mortar, shrink-proof, moderately expansive. Specifically for the filling of vacuums in the grouting of metal or wooden structures on vertical walls.
REPAR TIX BIC
Structural, thixotropic, fibre reinforced, two-component cement mortar Compared to REPAR TIX it is more adhesive with high waterproofing and moderately deformable.
REPAR TIX SFR
Monocomponent, thixotropic structural cement mortar, with added elastic metal fibres. Specifically for non-reinforced grout of considerable thickness, also in aggressive or high humidity environments.
REPAR TIX HG
Structural, thixotropic, fibre reinforced, monocomponent cement mortar with high performance. Specifically for marine, mountain and aggressive environment applications in general. Also ideal for wet shotcrete. Highly recommended!
REPAR TIX SPEEDY HP
Azichem has prepared an application protocol to create splendid floors that have optimum mechanical strength that are long-lasting with the aesthetic prestige of a natural floor.
Insulating plaster, dehumidifying, high thermo-acoustic performance
Chemical/mechanical hardener, anti-dust, nano-technology, non-pellicular