OSMOSANA

Mono-component, osmotic, rigid, ecological waterproofing

Code: OSM.0089

Components: 1

Appearance: Powder

Osmotic brushable hydraulic lime-based compound, for the construction of vertical barriers, waterproofing, in porous structure masonry (brick, natural stone, etc.) in ecological building interventions, new buildings and in the restoration of vintage buildings and monuments.

Functional categories
Customs Code
3824 5090

Certification obtained and Standards

Specification for Mortar for Masonry - General purpose rendering/plastering mortar (GP)

EN 998-1

Specification for Mortar for Masonry - General purpose rendering/plastering mortar (GP)

Product belonging to Sanageb, Azichem's product line dedicated to green-building, sustainability in constructions and bio-architecture since 1994.

Sanageb - Prodotti naturali per la Bioedilizia

Product belonging to Sanageb, Azichem's product line dedicated to green-building, sustainability in constructions and bio-architecture since 1994.

General characteristics

temperature-of-use

Temperature of use: +6 / +30 °C

mix-with-water

Mix with water: 24-36 %

shelf-life

Shelf-life: 12 months

maximum-diameter-of-aggregate

Maximum diameter of aggregate: 0.5 mm

min-recommended-thickness

Min. recommended thickness: 3 mm

solvent-free

Solvent-free

pot-life

Pot-life: 65 min

max-recommended-thickness

Max. recommended thickness: 5 mm

nonflammable

Nonflammable

uv-resistant

UV-resistant

Technical specifications

Density

1.580 kg/m³

Static elastic modulus

9000 N/mm²

Compressive strength

> 20 N/mm²

Capillary absorption

0.72 kg•h^0.5/m²

Coefficient of permeability

20.2 μ

Bonding force

1.4 N/mm²

Flexural strength

> 2.5 N/mm²

Available colours

- Light hazel

Characteristics

OSMOSANA is based on lime and hydraulic binders, botticino, kaolin, silica aggregates, tartaric acid, different silicates and carbonates. It has no traces of resins, solvents and radioemissive aggregates.

The hydraulic reaction of OSMOSANA produced by the natural chemical combination, of water lime and kaolin (metakaolin or industrial cocciopesto (lime mortar with crushed pottery)), also called "superpozzolanic" reactivity, is comparable to the hydration reaction of cement materials, but in ecological building key.

Use fields

Waterproofing treatments of brick or mixed external walls, provided they are sufficiently porous and absorbent and free from any waterproofing and / or water-repellent surface treatment, whether chemical (siloxanes, epoxies, polyurethanes, etc.) or natural (wax-up), before backfilling. Anti-capillary rising damp treatments in the construction of subbase screeds.

Preparation of supports

Application surfaces should be clean, free of soiling, crumbling and non-adhering parts, dust, etc., water repellent treatments in general, etc. conveniently saturated with water until they reach the condition "saturated with dry surface".

Use method

Pour about 2/3 of the mixing water into the mixer, add OSMOSANA and the remaining water; continue to mix until a homogeneous lump-free mixture is obtained. After mixing is completed wait a few minutes before applying.

Apply on site with a brush, spatula or roller, depending on the desired result. The mixing water indicatively necessary is 24-36% by weight (6-7 litres/bag for applications with the spatula, 8-9 litres/bag for applications by brush or roller).

Application methods

- Brush

- Spatula

- Low pressure airless nebulizer

Tool cleaning

- Water

Permitted supports

- Concrete

- Bricks

- Mixed walls (bricks and stones)

- Stone walls

Warnings, precautions and Ecology

Protect fresh surfaces from direct exposure to sunlight, from the rain and wind, cure the prolonged moist hardening.

Do not use for waterproofing works with negative hydraulic thrust.
Do not apply on little or non-porous substrates or previously coated with water-repellent treatments in general, if not after appropriate roughening by bush hammers, sanders and equipment suitable for preparatory treatments of substrates, or after appropriate treatment with suitable polymeric primers.

Share