Rheoplastic, thixotropic, structural, composite , reinforced fibre cement mortar, based on special cements, alkaline-resistant fibres, agents anti-carbonation, reactive fillers. selected siliceous aggregates. After hardening, it provides high-performance anti-carbonation protection, mechanical strength, watertightness, chemical-physical stability. Specific for filling cavities and embrasures produced by removing the blade caisson spacer, in concrete components in civil engineering, industrial and hydraulic works.
Specification for Mortar for Masonry - General purpose rendering/plastering mortar (GP)
Shelf-life: 12 months
Maximum diameter of aggregate: 1.5 mm
Min. recommended thickness: 0.8 mm
Pot-life: 40-45 min
Max. recommended thickness: 50 mm
Adhesion to the substrate: >2.5 N/mm²
Temperature of use: +5 / +35 °C
Mix with water: 14-16 %
Static elastic modulus
> 45 N/mm²
Adhesion to substrate
> 2.5 N/mm²
> 5 N/mm²
< 1.2 W/m*K
- Bag 25 kg
OSMOCEM AC is formulated with special agents capable of inhibiting or drastically reducing the motility carbon dioxide solutions in concrete, consequently ensuring very high anti-carbonation protection.
Approximately 19 kg/m² of OSMOCEM AC for every centimetre of thickness to be implemented (approximately 1900 kg per cubic metre).
Filling cavities and embrasures of blade caisson spacers, in concrete components in civil engineering, industrial and hydraulic works provided they are sufficiently porous and absorbent and free from any waterproofing and / or water-repellent surface treatment, whether chemical (siloxanes, epoxies, polyurethanes, etc.) or natural (wax-up).
Application surfaces should be clean, free of soiling, crumbling and non-adhering parts, dust, etc., water repellent treatments in general, etc. conveniently saturated with water until they reach the condition "saturated with dry surface".
Pour about 2/3 of the mixing water into the mixer, add OSMOCEM AC and the remaining water; continue to mix until a homogeneous lump-free mixture is obtained. The mixing water should be about 14%-16% by weight.
- Brick trowel
- Prefabricated concrete
Do not apply with direct exposure to sunlight and/or at temperatures below +5°C. Cure the protection and moist hardening of exposed surfaces.
Do not apply on little or non-porous substrates or previously coated with water-repellent treatments in general, if not after appropriate roughening by bush hammers, sanders and equipment suitable for preparatory treatments of substrates, or after appropriate treatment with suitable polymeric primers.
Two-component, osmotic cement, certified for drinking water and EN-14891. Moderately deformable, highly resistant and adhesive, it is a multi-use product. Resists traffic, UV rays, ideal for reinforced finishing coats. Azichem's bestseller!
Composed of flexible, two-component cement, certified for drinking water. Specifically for the waterproofing of terraces and balconies, applicable both on the screed and old floors.
Hard, monocomponent, osmotic cement. Highly resistant and adhesive. Specifically for the construction of reinforced, impermeable and thick grout, both in thrust and counter-thrust.
Hard, monocomponent, osmotic cement, certified for drinking water. Very adhesive and easy to apply. It is a classic osmotic mix, efficient and cheap!
Two-component, osmotic cement, slightly deformable. To use thick, both in thrust and counter-thrust. It is the evolution of the OSMOCEM MR, easier to apply and more adhesive. Recommended!
Hard, monocomponent, osmotic cement with a natural hydraulic lime base. It is an ideal product for waterproofing in positive thrust, in the restoration and recovery of old buildings.