MIKROSANA is a mixture of cement-free binders, recommended for injecting consolidation of brick, stone and mixed structures. Its hydraulic grip is based on the active lime-microsilica reaction and the presence of hydraulic calcium free of harmful soluble salts. Its exceptional fluidity, coupled with extremely small particle size, allows it to penetrate less than 1.5 mm pores and cracks. The addition of natural and artificial pozzolans allows progressive hydration and hardening beyond the standard 28 days of ripening. MIKROSANA, thanks to its particular constituents, is totally compatible with old mortars, which makes its use particularly recommended for the injection consolidation of antique plasters, even in the presence of frescoes.
Sanageb - Prodotti naturali per la Bioedilizia
Product of the Sanageb line, the line of products from Azichem Srl dedicated to green-building, ecological sanitation, thermal insulation and energy saving products since 1994.
Masonry mortars - Masonry mortar for general purposes (G)
Shelf-life: 12 months
Mix with water: 20-23 %
Maximum diameter of aggregate: 0.7 mm
Pot-life: 60 min
Permeability to water vapor
> 10 N/mm²
> 3 N/mm²
Water penetration after capillary absorption
Static elastic modulus
5000 - 7000 MPa
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
"• Extremely low hydration heat;
• High water vapour permeability;
• Low elastic modulus;
• Good mechanical resistance with slow and gradual mechanical resistance development;
• High support adhesion;
• Extremely fine binders and aggregates that allow high penetration crack and porous injections;
• Well-distributed structural consolidation and rebalancing across the entire masonry body;
• Compatibility with antique plasters and traditional materials;
• No expansive crystallization reactions or rejection by standard antique masonry materials;
• Absolutely no bleeding (mix water separation)."
Approximately 1550 kg of MIKROSANA for each cubic metre of volume to be filled.
"MIKROSANA is used for consolidating and re-adhesive injections of antique and frescoed plasters and as a grout for consolidation and rehabilitation injections of brick, stone and mixed structures.
Particularly recommended for antique wall structures with issues of compatibility between wall structure components and standard cement-based or epoxy-based reinforcement injections.
When applying consolidating injections in sizeable antique masonry volumes, it is recommended to avoid:
• The hardening of some injected areas faster than others (e.g. use of rapid hardening cement)
• Water vapour barriers that interfere with the normal breathability of the wall structure (e.g. use of epoxy resin injections);
• Stressing the wall structure with excessive heat build-up during the hardening of binding mixtures (e.g. use of extra-fine Portland cement).
• Chemical incompatibility with materials in the wall structure (e.g. potential formation of sulfoaluminates, such as ettringite and thaumasite, from the reaction between sulphates in the wall structure and Portland cement)."
"Before consolidating injections, joint grouting and masonry cracks must be sealed to prevent the injected material from leaking out. This can be done in the following ways:
• By providing, if plastering, a UNTERSANA rendering coat or plaster made on site using the natural hydraulic lime CALCESANA;
• By performing, if the masonry is to left exposed, perfect pointing of joints and discontinuities (e.g. cracks, dents, gaps) with one of the following mortars: SANAZIEG, SANALINK or UNISAN (to be chosen depending on the structural needs and characteristics of the antique mortars in the wall structure).
After sealing the discontinuities, make a pattern of holes, with a slightly downward incline, in correspondence with the mortar joints. Usually 4-6 holes are made per square metre with approximately 50cm separation and 20mm diameter. However, the exact arrangement and diameter of holes, angle of inclination, depth of penetration and any reinforcement of holes is to be decided by the designer and works manager, according to decisions based on structure type, degradation and intended result.
After blowing out disintegrated mortar and dust, wet the holes with water. Then insert plastic tubes (diameter 10 to 30 mm as needed) to convey the injection mixture well inside the holes. The tubes must be fixed to the masonry with one of the following mortars: SANAZIEG, SANALINK or UNISAN."
MIKROSANA mixing must be carried out with a high efficiency mechanical stirrer (e.g. twin-helix mixer with speed variator), with correct minimum/maximum water ratios (from 20% to 23% based on the weight of the premix), for at least three minutes. MIKROSANA acquires exceptional fluidity only after effective mixing. Once the desired consistency has been obtained, it is recommended to pass the mix through a 2 mm mesh sieve (or similar) to remove any lumps before injecting.
Injecting can be performed using gravity or mechanical means, from the lower holes first up to the higher ones, and with a pressure limited to sub 2 atm. If using mechanical means, pumping must be adjustable to low pressures. The mixture has a long useful life (> 1 hour), but it is recommended to keep it moving during work pauses and to stop using it after more than 3 hours, since, though not visible to the eye naked, it can begin to lose its exceptional fluidity and ability to penetrate into micro-cavities and micro-cracks."
- Mixed walls (bricks and stones)
- Stone walls
Power additive to create reinforced grout, injectable, to add to cement or hydraulic lime.
Cement grout (binary mix without aggregates), slightly expansive, ready for injection with low pressure or dropped into walls, with the sole addition of water. You are advised to use in walls built before 1900.
Micro-cement mortar, injectable, slightly expansive, for wall reinforcement and cavity filling, to use in grout solutions if the cavities are big or if high performance must be achieved.
Hydraulic lime based grout (binary mix without aggregates), slightly expansive, ready for injection with low pressure in walls, with the sole addition of water. Perfect for monument restorations of historic works.
Product similar to GROUT MICRO-J, specifically for sealing joints between block paving and natural stone flooring in general.