Castable, anti-leaching, shrinkage-compensated cement mortar

Code: GRT.0074

Components: 1

Appearance: Powder

Composite , castable, anti-washout, controlled shrinkage cement mortar, superfluid consistency, based on high-resistance cements, superpozzolanic fillers (MICROSIL 90), polymeric modifiers, shrinkage resistant agents, specific additives, calcium silicate mineral fibres, selected silica aggregates.

Linee di appartenenza

Certification obtained and Standards

Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)

EN 1504-3

Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)

General characteristics


Shelf-life: 12 months


Maximum diameter of aggregate: 5 mm




Highlighted product


Pot-life: 120 min


Mix with water: 14-16 %




Temperature of use: +5 / +35 °C

Technical specifications

Skid resistance

54 mm

Chloride content

<0.01 %

Static elastic modulus

26000 N/mm²


>12 _

Determination of thermal compatibility

2.5 mPa

Resistance to carbonatation

3 mm

Compressive strength

> 58 N/mm²

Reaction to fire

A1 _

Bonding force

2.6 N/mm²

Capillary absorption

0.43 kg•h^0.5/m²

Flexural strength

> 8 N/mm²


2085 kg/m³

Available colours

- Gray

Packaging and dimensions

- Bag 25 kg

- Pallet: 50 x (Bag 25 kg)


- Based on of thickened silica fume
- three-dimensionally reinforced fibre with mineral and synthetic fibres
- Provides high adherence and adhesion
- dimensionally stable (shrinkage-compensated)
- Provides high stability-physical chemical and resistance to chlorides and sulphates
- suitable for underwater castings: it is anti-washout
- high strength in terms of hydrostatic positive and negative thrust


Approximately 19,50 kg/m² of GROUT CR for every centimetre of thickness to be implemented (approximately 1950 kg per cubic metre).

Use fields

Repair and protective coatings of hydraulic structures, marine and underwater structures, and articles in critical situations: harsh chemical-physical, leaching water, marine atmosphere, etc. Filling of formwork for the containment of cast immersed in sea water.

Preparation of supports

In case of underwater application, the installation operations must be carried out within 8-10 hours of cleaning and "fouling" (accumulation and deposits of organic and inorganic particles on product surfaces) removal.

Use method

Pour 2/3 of total mixture water in the cement mixer, gradually add the product and the remaining water, until a homogeneous mixture of the required consistency is obtained.
For sizable filling thicknesses, greater than 60 mm, GHIAIETTO 6.10 (inert washed is selected with a particle size of from 6-10 mm) can be added in a percentage ranging from 20% to 40 %, on the basis of practical requirements.
In some particularly demanding cases in terms of the resistance to the "dry-wet" cycle (for example, for the action of the tides) or for chemical attacks particularly strong, it would be advisable to add, in addition to the gravel, even thickened silica fume(MICROSIL 90), and in a variable amount depending on the thickness and construction-related need, to further improve the waterproofing and the mechanical strength of the product. In these cases, please contact our Technical Service.

Application methods

- Pour out

- Pump

- Brick trowel

- Finishing trowel

- Spatula

Tool cleaning

- Water

Permitted supports

- Concrete

- Bricks

- Mixed walls (bricks and stones)

- Stone walls

Warnings, precautions and Ecology

Thermal range of application and conservation: +5/ +35 °C; do not apply in case of direct exposure to sunlight. Cure the protection and the moist hardening of exposed surfaces. In the case of casts in water, make sure of perfect product hardening before removal of the formwork.


Products on display

  • Osmocem
  • Syntech H.A.G.
  • Sanawarme