Code: GRT.0262
Components: 1
Appearance: Powder
Shrink-proof, rheoplastic, pouring mortar for precision anchorage of operating machines, turbines, rolling mills, overhead cranes, etc.. With a cement binding base, super-lubricating agent, shrink-proof compounds, select aggregates, fibre-reinforced with a mix of steel and polypropylene fibres and super-pozzolanic reactive fillers.
Density: 2.200 kg/dm³
Max. recommended thickness: 15 cm
Maximum diameter of aggregate: 2 mm
Mix with water: 15 %
Nonflammable
Pot-life: 30 min
Shelf-life: 12 months
Temperature of use: +5 / +35 °C
Bonding force
2.4 MPa
Compressive strength
70.03 N/mm²
Flexural strength
10.3 N/mm²
Reaction to fire
A1 _
- Gray
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
Approximately 1900 kg of GROUT 2 SFR for every cubic metre of mixture to be made.
Precision anchorage of operating machines: presses, turbines, power supply units, rolling mills, alternators, overhead cranes, metal structures, tracks, etc.. Structural adaptation, renovations, drawing and reinforcements, using injections and castings inside formworks. Creation of connection anchorage using steel bars with a diameter and depth consistent with the project specifications, by casting in specifically prepared perforations. Construction of structural road joints.
The application surfaces should be clean, free of containment, inconsistent and incoherent parts, dust, etc., conveniently saturated with water to reach the "saturated to dry surface" condition.
Place 2/3 (approx 2.5 litres per bag) of the total water in the mix, then gradually add the product and the remaining water, mixing until you obtain an even mix with the desired consistency and no lumps.
- Pour out
- Water
- Concrete
- Prefabricated concrete
- Mixed walls (bricks and stones)
- Rusty reinforcement rods
Given the self-levelling properties of the product and its self-compacting capacity, you are advised to pay due attention to the vibration phase. Excess zeal in the vibration operation could worsen the aesthetic performance of the resulting manufactured work.
Do not use in the absence of adequate side confinements.
Ensure protection and damp seasoning of the surfaces exposed.
Implement casting procedures capable of ensuring the absence of vacuums and cracks; grout the mortar from one part of the perimeter of the casting to avoid air sacks.