FLOOR TENAX SFR is a quick-hardening, plastic/fluid, pourable mortar that can be used for repairs on deteriorated floors, structural repairs of reinforced concrete with increased ductility, very low level regularization (5-10 mm) of radiant floors. The formulation contains very high strength ultra-fine cements, micro-silicas with pozzolanic activity, aggregated in a rational granulometric curve (0.1 ÷ 2.0 mm), special additives and brass-plated metallic microfibres READYMESH MR-060. The special shape coefficient and the particular surface conformation of this fibre, give the applied product an exceptional reduction of the hygrometric shrinkage, the dissipation of the efforts in the case of heavy stresses and a high thermal conductivity. The product mixes with very low water/binder ratios (<0.32). The special formulation of FLOOR TENAX SFR allows a fluid plastic rheology free of bleeding and segregation, giving the restorations performed: mechanical strength, fracture energy, exceptional durability and very high chemical-physical resistance.
Screed material and floor screeds - Screed material - Properties and requirements
Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)
Max. recommended thickness: 25 mm
Min. recommended thickness: 8 mm
Mix with water: 11 - 12.5 %
Shelf-life: 12 months
Temperature of use: +5 / +30 °C
> 35 N/mm²
> 2.5 N/mm²
Breaking load longitudinal
Compressive strength after 12 hours
Compressive strength after 28 days
> 95 N/mm²
Flexural strength after 28 days
> 15 N/mm²
Flexural strength at 01 day
> 9 N/mm²
Static elastic modulus
- Bag 25 kg
FLOOR TENAX SFR has a workability time of approximately >120 minutes, after which the gripping process is triggered followed by a progressive hardening. The hygrometric shrinkage is extremely limited, guaranteeing volumetric stability to restoration carried out. The performances that make FLOOR TENAX SFR unique are:
• resistance to dynamic stress,
• fatigue resistance, fracture energy, toughness and resistance to post-breaking strain,
• very high mechanical compression strength (> 95 MPa at 28 days),
• very high mechanical tensile and bending strength (> 15 MPa at 28 days),
• excellent durability and resistance to chemical attacks.
Recommended maximum thickness: 25 mm (flooring) 50 mm (casting in formwork)
Minimum recommended thickness: 5 mm (flooring) 25 mm (casting in formwork)
Approximately 22 kg/m² of FLOOR TENAX SFR for every centimetre of thickness to be implemented (approximately 2200 kg per cubic metre).
FLOOR TENAX SFR is used in in structural reinforcements and repair of deteriorated floorings with limited thickness (typical applications
in the range 8 - 20 mm), characterised by high performance in terms of deformation, resistance and anti-cracking resistance. The main application fields are:
• repair of industrial concrete floors with walkability allowed after approximately 24 hours from casting and drive over allowed after 48-72 hours depending on the temperature at the time of application
• repair of joints in industrial flooring;
• laying and fixing of manhole covers;
• reinforcement of floors with the low thickness estradossal hood technique;
• any kind of structural repair and restoration performed with casting within formwork such as for example the cladding of pilates and beams; in this case the maximum recommended thickness can be up to 40-50 mm (for higher thicknesses we recommend the addition of GHIAIETTO 6.10 with addition percentages that can vary from 20 to 40%; in these cases ask our service technical advice on the correct addition percentages).
• regularization of radiant flooring substrates with coatings starting from 5 mm thick (recommended thickness from 5 to 10 mm), characterized by high values of thermal conductivity and reduction of shrinkage.
Application surfaces must be clean, free of dust, contamination, crumbling, inconsistencies, etc., and adequately saturated-surface-dry with water.
• The support must be prepared by mechanical scarification or hydro-scarification for a depth of not less than 6 mm. The scarification of the support is an absolutely necessary operation to ensure sufficient grip of the coating applied. In the case of localized patches or repairs, cut the contours at right angles with an angle grinder.
• The support must not have traces of oils, greases, detergents.
• The support must be in good condition, clean, course, without crumbling parts or dust (suction of all dust and debris with an adequately equipped vacuum system). Wash the surface with pressurized water. Saturate the support with water before applying and eliminate any excess water on the surface.
• Application temperature: 5°C to 30°C.
• We strongly recommend the use of a vertical axis mixer with planetary or double horizontal helical movement, both for effective mixing of fibre-reinforced reinforcement and for optimal performance of site operations.
• MIXING: mix the entire contents of the bag with potable water in the measure of 11% - 12.5% referred to the total weight of the mortar (about 2.75 - 3.13 lt per 25 kg bag) creating a homogeneous mixture. Mixing time: approximately 4 minutes with high-efficiency mixer.
• In the case of large thicknesses (e.g.: manhole repairs) use compaction with a vibrating needle or tamp it down in a very intense way.
• Level the surface with a vibrating screed on the prepared templates.
• The surface must be protected after application by polyethylene sheets or anti-evaporation
treatments. The latter should be sprayed on the restored surface as soon as the hardening phase begins (provide anti-evaporation treatments only if no other protective or aesthetic-protective applications are planned above: contact our technical service for advice on the most indicated surface protection methods and on the type of product that can be used as a curing compound).
In the case of thicknesses exceeding 20 mm, FLOOR TENAX SFR must be laid out, supported and floated on a suitable sub-base only with appropriate measures to ensure the structural adhesion and anchoring to the support itself. The methods of anchorage suggested include: laying with a special epoxy resin for structural construction joints (SYNTECH RGS or SYNTECH PAVISHEER); or positioning a galvanized steel net with 5x5 cm mesh and 2 mm wire, which is spaced from the support plane of half the expected thickness of FLOOR TENAX SFR and anchored to the same by "L"-shaped connectors fixed in holes resinated with SYNTECH PROFIX or fixed by nailing with "nail guns".
Provide a cover with wet TNT and waterproof sheet as soon as the surfaces are walkable and keep the surfaces covered for at least 48 hours.
It is always important to carry out preliminary tests to check the appropriateness of the product, depending on specific requirements. It is recommended to treat carefully the curing of the shotcrete for a few days, through continuous flushing of water or covering the same with a length of cloth made of polyethylene (winter period) or awning in non-woven fabric impregnated with water (spring/summer).
- Finishing trowel
- Straight edge