Thermal coating plaster, macroporous, with high thermal and acoustic insulation, average density equal to about 540 kg/m³, based on hydraulic lime, expanded perlite, granulated cork and specific and anti-saline agents, for dehumidification, thermal and hygrometric recovery of buildings and walls in ecological building interventions, new buildings and in the restoration of vintage buildings and monuments. Specific for applying "mineral coatings".
UNI EN 998-1 (T)
Specification for Mortar for Masonry - Mortars for thermal insulation (T)
Sanageb - Prodotti naturali per la Bioedilizia
Product belonging to Sanageb, Azichem's product line dedicated to green-building, sustainability in constructions and bio-architecture since 1994.
To be applied in two coats
Max. recommended thickness: 10 cm
Material 100% eco-friendly
Shelf-life: 12 months
To be applied in three coats
Temperature of use: +8 / +30 °C
Mix with water: 43-53 %
Pot-life: 60 - 75 min
Maximum diameter of aggregate: 2.5 mm
Min. recommended thickness: 3 cm
Static elastic modulus
< 3000 N/mm²
Reaction to fire
> 1.5 N/mm²
- Light hazel
SANAWARME is the highest technological expression of Azichem in the context of renovating plasters. It is a product based on hydraulic lime, botticino, kaolin, calcium caseinate, Vichy salt, calcium carbonate, tartaric acid, ammonium salts, expanded perlite, cork powder and natural fibres. SANAWARME is characterised by high hygroscopic, breathable and thermal/acoustic insulation properties. It is a "thermal mineral coating", natural, for ecological building, that does not contain cements, resins, solvents and radioemissive materials.
The structure of the coatings made with SANAWARME, which is particularly suited to quieten and dissipate, in the form of heat, the acoustic energy inside the pores and "channels", provides interesting performance even in terms of sound absorption which, at high frequencies, reaches values of 1/3, with interesting prospects for acoustic correction of the internal environment (Test Report no. 214705 of August 3, 2006 issued by the institute Giordano).
Applying coating plasters in both new constructions, and in interventions of restoration and renovation of old buildings. Anti-condensation and mildewcide correction for indoor, out of the ground and buried surfaces. Insulation of thermal bridges.
Removal of crumbling plaster, if present. The wall bodies for application should in any case be clean, intact, free from fouling, dust, crumbling and non-adhering parts, conveniently saturated with water until it reaches the condition of "saturated dry surface".
In the presence of salt efflorescence it will be necessary to ensure its careful removal by application of packs of the specific acid detergent and saline converter DETERG-A, in solution with water 1:4. To prevent any new spills of salts, use specific universal anti-saline treatments in aqueous solution, SANAREG, for humid surfaces, or solvent-based, FEST SALZ, for cohesive saline concretions but with perfectly dry surfaces.
Preliminary construction of specific anchoring scratch coats, breathable, made with UNTERSANA. The rendering, applied by "spraying", must provide a rough, corrugated surface, designed to promote the bonding of the subsequent plaster, which must be applied no later than 2-3 days. In the case of wooden surfaces, attach a galvanized steel wire mesh, diameter 2 mm and mesh 5x5 cm, to the support, holding it away from the surface by 2-3 mm. Spray the rendering UNTERSANA by hand or by plastering machine, in order to provide a rough surface, designed to facilitate the application and the adhesion of SANAWARME. In the case of applying the thermal coat SANAWARME on existing plaster, it is recommended to apply the super-adhesive rendering SANAPLUG.
Prepare the plaster, adding SANAWARME, to the mixing water, for approximately 60-70% by weight (8.5 -9 litres per 13 kg bag). Mix thoroughly until it reaches a smooth, creamy, lightweight, lump-free mixture resembling a "compact foam". Apply the thickness required according to the thermal calculation by plastering machine (type PFT model G4, or the like, equipped with lung for light plasters). For small sizes it is also possible to apply it manually with straight edge and plastic mortar.
Regularise the plastered surfaces with fine skim SANASTOF for ecological buildings, for an indicative consumption of 4 kg/m². "Drown" in the thickness of the finishing layer the fibreglass mesh ARMAGLASS 160. Successive breathable paints or putty coats (from the series SANAFARBE, SANAXIL or PROTECH SIL) can be applied after approximately 28 days; in any case, after the proper curing of the plaster, depending on the actual environmental conditions, and the loss of initial alkalinity.
- Finishing trowel
- Plastering machine
- Straight edge
- Cement-based or lime-based mortars
- Prefabricated concrete
- Mixed walls (bricks and stones)
- Stone walls
The fresh surfaces, of the plaster set on-site , should be protected from direct exposure to sunlight, from the rain and the wind and must be cured by prolonged moist hardening.
Over 4cm thick, inclusive of UNTERSANA, SANAWARME and SANASTOF, it is appropriate to insert in the centre thickness of SANAWARME a galvanized steel wire mesh, diameter 2 mm and mesh 5x5 cm, fixed to the masonry by steel connectors with improved adherence, following a square lattice with 1 metre spacing.
Dehumidifying, thermo-insulating plaster (800 kg/m³), with a natural hydraulic lime base. Ideal for hygrometric, anti-condensate renovation of internal walls (overground and underground).
Breathable plaster (1500 kg/m³), with a natural hydraulic lime base. Ideal for plastering overground or underground walls, both indoors and outdoors.
Dehumidifying plaster (1200 kg/m³), with a natural hydraulic lime base. Ideal for hygrometric renovation of external walls. Recommended!
Structural plaster (1700 kg/m³), dehumidifying, with a grey cement base. Ideal for reinforced grout on old walls.
Structural plaster (1700 kg/m³), dehumidifying, with a pure white cement base. Ideal for reinforced grout on old walls and the re-construction of overhanging roofs, belt courses, cornices, etc.